Polyacrylonitrile, also known as polyvinyl cyanide and Creslan 61, is a synthetic, semicrystalline organic polymerresin, with the linear formula n. Though it is thermoplastic, it does not melt under normal conditions. It degrades before melting. It melts above 300 °C if the heating rates are 50 degrees per minute or above. Almost all PAN resins are copolymers made from mixtures of monomers with acrylonitrile as the main monomer. It is a versatile polymer used to produce large variety of products including ultra filtration membranes, hollow fibers for reverse osmosis, fibers for textiles, oxidized PAN fibers. PAN fibers are the chemical precursor of high-quality carbon fiber. PAN is first thermally oxidized in air at 230 °C to form an oxidized PAN fiber and then carbonized above 1000 °C in inert atmosphere to make carbon fibers found in a variety of both high-tech and common daily applications such as civil and military aircraft primary and secondary structures, missiles, solid propellant rocket motors, pressure vessels, fishing rods, tennis rackets and bicycle frames. It is a component repeat unit in several important copolymers, such as styrene-acrylonitrile and acrylonitrile butadiene styrene plastic.
History
Polyacrylonitrile was first synthesized in 1930 by Hans Fikentscher and Claus Heuck in the Ludwigshafen works of the German chemical conglomerate IG Farben. However, as PAN is non-fusible, and did not dissolve in any of the industrial solvents being used at the time, further research into the material was halted. In 1931, Herbert Rein, head of polymer fiber chemistry at the Bitterfeld plant of IG Farben, obtained a sample of PAN while visiting the Ludwigshafen works. He found that pyridinium benzylchloride, an ionic liquid, would dissolve PAN. He spun the first fibers based on PAN in 1938, using aqueous solutions of quaternary ammoniumsodium thiocyanate and aluminum perchlorate for the production process and considered other solvents including DMF. However, commercial introduction was delayed due to the wartime stresses on infrastructure, inability to melt the polymer without degradation, and solvents to allow solution processing were not known yet. The first mass production run of PAN fiber was in 1946 by American chemical conglomerate DuPont. The Germanintellectual property had been stolen in Operation Paperclip. The product, branded as Orlon, was based on a patent filed exactly seven days after a nearly identical German claim.
Most commercial methods for the synthesis of PAN are based on free radical polymerization of acrylonitrile. In most of the cases, small amount of other vinyl comonomers are also used along with AN depending on the final application. Anionic polymerization also can be used for synthesizing PAN. For textile applications, molecular weight in the range of 40,000 to 70,000 is used. For producing carbon fiber higher molecular weight is desired. In the production of carbon fibers containing 600 tex PAN tow, the linear density of filaments is 0.12 tex and the filament diameter is 11.6 µm which produces a carbon fiber that has the filament strength of 417 kgf/mm2 and binder content of 38.6%. This data is demonstrated in the Indexes for Experimental Batches of PAN Precursor and Carbon Fibers Made from It table.
Applications
Homopolymers of polyacrylonitrile have been used as fibers in hot gas filtration systems, outdoor awnings, sails for yachts, and fiber-reinforced concrete. Copolymers containing polyacrylonitrile are often used as fibers to make knitted clothing like socks and sweaters, as well as outdoor products like tents and similar items. If the label of a piece of clothing says "acrylic", then it is made out of some copolymer of polyacrylonitrile. It was made into spun fiber at DuPont in 1942 and marketed under the name of Orlon. Acrylonitrile is commonly employed as a comonomer with styrene, e.g. acrylonitrile, styrene and acrylate plastics. Labeling of items of clothing with acrylic means the polymer consists of at least 85% acrylonitrile as monomer. A typical comonomer is vinyl acetate, which can be solution-spun readily to obtain fibers that soften enough to allow penetration by dyes. The advantages of the use of these acrylics is that they are low-cost compared to natural fibre, they offer better sunlight resistance and have superior resistance to attack by moths. Acrylics modified with halogen-containing comonomers are classified as modacrylics, which by definition contain more than PAN percentages between 35-85%. Incorporation of halogen groups increases the flame resistance of the fibre, which makes modacrylics suitable for the use in sleepwear, tents and blankets. However, the disadvantage of these products is that they are costly and can shrink after drying. PAN absorbs many metal ions and aids the application of absorption materials. Polymers containing amidoxime groups can be used for the treatment of metals because of the polymers’ complex-forming capabilities with metal ions. PAN has properties involving low density, thermal stability, high strength and modulus of elasticity. These unique properties have made PAN an essential polymer in high tech. Its high tensile strength and tensile modulus are established by fiber sizing, coatings, production processes, and PAN's fiber chemistry. Its mechanical properties derived are important in composite structures for military and commercial aircraft.
Carbon fiber
Polyacrylonitrile is used as the precursor for 90% of carbon fiber production. Approximately 20-25% of Boeing and Airbus wide-body airframes are carbon fibers. However, applications are limited by PAN's high price of around $15/lb.
Oxidized Polyacrylonitrile Fiber (OPF)
Oxidized PAN Fiber is used to produce inherently flame resistant fabrics. Commonly when it is used in FR fabrics for protective apparel it is referred to as OPF and is a high-performance & cost-effective flame and heat resistance solution. OPF can be considered one of the most FR fabrics commercially produced since it has an LOI in the range of 45%-55% which is one of the highest LOI ranges available as compared with other common FR fabrics which have lower LOI values ; and OPF also demonstrates the lowest toxic gas generation upon burning as compared with other common fabrics.