Joint compound


Joint compound is a white powder of primarily gypsum dust mixed with water to form a mud the consistency of cake frosting, which is used with paper or fiber joint tape to seal joints between sheets of drywall to create a seamless base for paint on interior walls. It is often referred to simply as mud or as joint cement

Drying type

Drying type joint compounds are vinyl based and harden when they dry by evaporation.

Ready-mix lightweight joint compound

Ready-mix lightweight joint compound is a pre-made form of joint compound designed for fast application and easy maintenance. The compound is a complex combination often including water, limestone, expanded perlite, ethylene-vinyl acetate polymer, attapulgite, and other ingredients. The delicate mixture of compounds gives it a creamy texture that spreads easily onto drywall surfaces and then hardens as the moisture evaporates. Drying type compound takes a long time to dry out and is used to fill holes or gaps and shrinks as it drys, possibly producing cracks in thick applications. Ready-mix joint compound is usually more forgiving than the setting type of joint compound. It can be used for as long a period of time as needed, and does not dry up unless left unattended for a long period of time, but must be kept from freezing. This type of compounds should be used at temperatures above and all of the materials should be a similar temperature.
There are mainly three types of premixed joint compounds.
1 premixed taping compound which is using for bedding and taping coat.
2 Finishing or topping compound which is using for filling and finishing coats.
3 All purpose joint compound which can be used in bedding and taping coat, filling and finishing coats.

Powdered drying type

Powdered drying type compounds are available.

Setting type

Setting type joint compounds come in powder form and are mixed with water immediately before use. This type contains plaster of paris and sets through a chemical hardening process rather than evaporation, which gives it an advantage in filling holes and gaps that would take many days to dry out and have shrinkage cracks using the drying compound. Setting type compounds are available in setting times ranging from 5 to 210 minutes and types that bond extremely well and are very hard and types that are soft and easy to sand. Once mixed with water, the setting type must be used before it sets; any leftover is wasted and if not enough is mixed, another batch is needed to finish the job, and all tools must be very clean or the compound may set up prematurely. This makes the setting type compounds harder and more time consuming to prepare, but they set quickly. Setting type compounds can be used at temperatures down to. Some drywall professionals use setting type mud for the first coat and a drying type for the thinner finish coat. Setting type compounds do not soften when they get wet, thus are better for moist environments, such as bathrooms.

Special types

Walls built to slow the spread of fire are called a firewall and are sometimes built using special fire-resistant drywall. Special joint compound for use with fire rated drywall is needed.
Reduced dust formulas cause the dust particles to clump together falling out of the air sooner than regular formulas, thus reducing airborne dust.
Moisture- and mold-resistant formulas are available.
Tapeless drywall joint compound
In recent years, some companies in Europe, Australia and Canada have developed a new type of drywall joint compound called tapeless joint compound. It can be applied to the joints directly without either paper tape or fibreglass mesh tape. It can save about 30% of labour time for finishing the drywall joints.
So far, every tapeless joint compound is setting compound. There are two type of tapeless setting compound: one is setting compound reinforced by some very strong chemical glues. The other is fibre reinforced setting compound.
Lately a Canadian company has developed a fiber-reinforcement additive which can be mixed with either setting or air-drying premixed drywall joint compounds and turn the regular drywall joint compounds to tapeless joint compounds.

Usage

Ready-mixed joint compound is most commonly used in hanging drywall for new or remodeled homes. Application is simple and easy, usually never taking more than three or four coats. When used for new walls, joint compound effectively eliminates all blemishes from the surface of the drywall, such as fasteners, damage, or drywall tape. Joint compound is used to finish gypsum panel joints, corner bead, trim and fasteners, as well as skim coating. In addition, it is also very handy for fixing minor blemishes or damages to walls. It easily patches up holes, bumps, tears, and other minor damage.
Often referred to as drywall taping mud, joint compound is the primary material used in the drywall industry by a tradesperson, or applicator, called a "drywall mechanic," "taper," or "drywall taper." A similar compound is used in various ways as a sprayed-on textural finishing for gypsum panel walls and ceilings that have been pre-sealed and coated with joint compound. The flexibility and plastic qualities of joint compound make it a very versatile material both as sealer or finishing coat for wall surfaces, and also in decorative applications that range from machine sprayed texturing to hand-trowelled or even hand-crafted and sculptural finishes. In North America the application of joint mud and drywall tape sealer and trowelled joint compound on gypsum panels is a standard construction technique for painted wall and ceiling surfaces. Until more recently in North America, and through the world, several different plasters such as veneer plaster and "plaster of Paris" have been used in a similar ways to joint compounds as fillers or for decorative purposes since ancient times, and the actual make up and working properties of these compounds is much similar. Modern ready-mixes or powder and water mixes are available in a wide range of styles from slow-drying to quick-drying to suit specific demands for use by contractors or decorators.
Mudding is usually done in three layers and it is important to use the correct type of mud for the first and last layer though a multi-purpose compound may be adequate for all coats: Bedding coat or taping coat where the mud is applied to seams and corners and paper joint tape is pressed into the mud. The mud used here needs to adhere well and be strong and is called a taping compound; filler coat where the tape is covered and roughly smoothed; and the finish coat or topping coat which is very smooth. A topping compound is soft, smooth and easy to sand. Some sanding of the finish coat is usually required to get a smooth surface. Sheets of drywall usually have tapered edges to provide space for the thickness of the tape and mud at the seams.
While joint compounds are used for bedding tape and initial layers overtop, it is best to apply topping compound for finish layer that level and sand more evenly. Both require thinning for practical application.
Applying and sanding compound is messy work and finished surfaces, such as floors, and air handling ducts need to be covered.
Pock marks are a defect caused by air bubbles which form after joint compound is applied. The bubbles are caused by the inability of moisture to be absorbed into the surface such as when the surface is already painted, has a layer of grease or cigarette smoke, or a drying-type compound applied over a dense, setting-type compound. The moisture exits through the finished surface making bubbles which dry as pock marks. The bubbles can be reworked while the compound is drying to get a smooth surface. Commercial additives are designed to reduce pock marks or the use of dish soap mixed into the mud. However, these products reduce bonding so they should not be used on the bed coat.

Health concerns

Construction workers who sand drywall joint compound are often exposed to high concentrations of dusts, talc, calcite, mica, gypsum, and in some cases, respirable silica.
Some of these have been associated with varying degrees of eye, nose, throat, and respiratory tract irritation.
Over time, breathing the dust from drywall joint compounds may cause persistent throat and airway irritation, coughing, phlegm production, and breathing difficulties similar to asthma. When silica is present, workers may also face an increased risk of silicosis and lung cancer.
Joint compound mixes manufactured prior to the 1980s often contained a complex mixture of several substances. Among the additives used were asbestos fibers, which provided cohesiveness. Exposure to friable asbestos increases risks of various serious health conditions, including cancer. Joint compounds manufactured from 1980 onward were required to have asbestos removed in favor of other compounds, due to legislation banning widespread use of asbestos.
For all of these reasons, constant use of a respirator is recommended by almost all drywall compound manufacturers and is required by some labor authorities.