The Composition C family is a family of related US-specified plastic explosives consisting primarily of RDX. All can be moulded by hand for use in demolition work and packed by hand into shaped charge devices. Variants have different proportions and plasticisers and include composition C-2, composition C-3, and composition C-4.
History
The term composition is used for any explosive material compounded from several ingredients. In particular, in the 1940s the format "Composition " was used for various compositions of the novel explosive RDX, such as Composition B and other variants.
Development
The original material was developed by the British during World War II, and was used in the Gammon bomb. It was standardised as Composition C when introduced to US service. This material consisted of 88.3% RDX and a mineral oil-based plasticiser and phlegmatiser. It suffered from a relatively limited range of serviceable temperatures, and was replaced by Composition C-2 around 1943.
Composition
Composition C-1 contained a slightly smaller proportion of RDX, but used an explosive plasticiser, which contained tetryl, nitrocellulose and a mixture of nitroaromatics produced during the manufacture of TNT, and a trace of solvent.
Characteristics and Usage
Composition C-3 was very similar to Composition C-1, but removed the solvent and varied the exact proportions of plasticisers to improve high temperature storage. It is a yellow, putty-like material. It remained a service item through the Korean War, but had marginal plasticity at the very low temperatures encountered in Korean winters, and was significantly toxic, including by vapour and skin absorption. While Composition C-3 had a much wider serviceable temperature range than Composition C, it could not be stored at elevated temperatures. Consequently, it was replaced around 1944 by Composition C-4. The velocity of detonation is about 7600 m/s Composition C-3 consists of 77%–85% cyclonite and 15%–23% gel made out of liquid nitro compounds and nitrocellulose or butyl phthalate and nitrocellulose. One of the first reported and tested compositions of C-3 was very similar to earlier Composition C-2 and contained 77% RDX, 3% tetryl, 4% TNT, 1% NC, 5% NT, and 10% DNT. The last two compounds are oily liquids and plasticise the mixture. The most important later innovation of C-3 introduced the non-explosive plasticiser butyl phthalate instead of this mixture of nitro compounds. This reduced the toxicity while increasing the concentration of RDX and improving safety of use and storage. It also opened the way to begin study of new non-explosive low-toxicity plasticisers and binder.
Discovery
Research on a replacement for C-2 was begun prior to 1950, but the new material, new generation of Composition C, did not begin pilot production until 1956.
~5.3% of di-sebacate, sometimes it was replaced partly by similar compounds such as dioctyl adipate
less than 0.6% of water
It is less volatile than C-4 and has less tendency to harden at low temperature. It has a density 1.48–1.60g/ml, does not become hard even at −55 °C, and does not exude at +77 °C. C4 has a detonation velocity of 8092 m/s at high density and velocity of 7550 m/s at low density 1.48 g/ml. It is so successful that it remains in army service up to the current time without any significant changes.